•Ni incorporated Al2O3-zeolite beta composites were synthesized via facile one-step method.•Al2O3 to BZ affects Ni particle size, Al local environments and acid sites.•31P NMR revealed that Bronsted to Lewis acid ratio dramatically altered with Al2O3 addition•Al2O3 modified Ni composites exhibit superior catalytic performance in HDO of palm oil.•Strong metal-support interactions prevent sintering of Ni particles and less coke formation
The hydrodeoxygenation (HDO) of bio-oil is one of the potential approaches to produce green diesel. However, HDO catalyst requires the development of bifunctionality which translates to the simultaneous presence of acidic and metal sites for desired catalytic activity and selectivity. Zeolites and their composites are attractive candidates for the conversion of biomass to fuels. In the present work, a series of Ni-incorporated Al2O3-zeolite beta bifunctional composite catalysts with distinct Al2O3 (25–75 wt%) and Ni contents (5–15 wt%) were synthesized via a facile one-pot method directly from nickel acetate, nano-boehmite (γ-AlO(OH)) and the NH4+ form of beta zeolite (NH4+-BZ). The nano-boehmite particles, due to the positive charges on their surface, electrostatically attract negatively charged beta zeolite crystals, which leads to the assembly of a hierarchical pore structure upon calcination. Interestingly, the composite catalysts synthesized were quite homogeneous with uniform dispersion of Ni particles. All composite catalysts were thoroughly characterized using XRD, SEM-EDX, SEM-mapping, HR-TEM, H2-TPR, H2-TPD, NH3-TPD, XPS, 31P MAS NMR, 27Al MAS NMR and N2 sorption analysis. The synthesized composite catalysts with distinct Al2O3 contents showed diverse textural properties, distinct nature of acid sites and improved performance in hydrodeoxygenation of palm oil. Particularly, the Ni/BZ-Al50 (with BZ:Al2O3 = 50:50) composite catalyst significantly enhanced the conversion of palm oil (up to 90%) and yield of n-C15-C18 hydrocarbons (up to 69%) at moderate temperature of 375 °C as compared to 10Ni/BZ catalyst (Conv. = 75%, yield of n-C15-C18 = 52%). The higher catalytic performance realized with composite catalysts can be ascribed to its hierarchical pore structure, moderate acidity (chemisorption studies), tuned acid sites nature (solid state NMR) and homogeneous distribution of active Ni sites (H2 chemisorption) which helps to improve product selectivity by minimizing side reactions. The time-on-stream (TOS) experiments were carried out up to 20 h which clearly showed that composite catalysts are more stable suggesting the lower amount of coke deposition (TPO studies) and suppression of metal sintering.