Abstract
Composites consisting of an alumina matrix and 20 vol.% transition metal (Ni or Fe) particles, prepared by hot pressing powder blends, have been studied using spatially resolved transmission electron energy-loss spectroscopy (EELS), and, to a lesser extent, by high-resolution electron microscopy (HREM). Particular attention was paid to the elucidation of the chemical bonding mechanisms at the metal-ceramic interface; EELS spectra from interfacial regions being obtained via a spatial difference technique. From both qualitative and quantitative interpretation of EELS near-edge structures, as well as observed HREM images, the data appear to be consistent with the presence of an Al-terminated alumina at the interface and the formation of direct transition metal - aluminium bonds in Al(O3M) (M = Ni or Fe) tetrahedral units, possibly as a result of the dissolution and interfacial reprecipitation of Al during processing. These results correlate well with similar model studies on diffusion-bonded Nb/Al2O3 interfaces and may, in the light of recent theoretical electronic structure calculations, have implications for the resultant interfacial bond strength in such materials.