Abstract
This paper considers the effects of an atmospheric plasma treatment (APT) on the surface properties of an amine cured carbon fibre/epoxy resin composite, and how those effects manifest over time. In particular, the ability of the APT to remove a thin layer of silicone-containing, proprietary, release agent (Chemlease® 41 EZ), typically used in the production of composite components, has been investigated. It was concluded that the reduction in water contact angle (WCA) after APT for both the solvent wiped and contaminated surfaces was as a result of an increase in oxygen containing species at the surface, as determined through X-ray photoelectron spectroscopy (XPS). Further, it was found that the APT slightly reduced the failure strength of lap shear specimens for solvent wiped surfaces, whereas an increase in failure strength was observed for silicone contaminated samples. WCA and XPS results suggest that the contaminant layer was not removed, but instead transformed to a more stable inorganic form.