The carrier transport of carefully purified regioregular poly(3-hexylthiophene) films was studied using time-of-flight photocurrent measurements. The authors find balanced ambipolar transport with a room-temp. mobility for holes of 3 * 10-4 cm2 V-1 s-1 and for electrons of 1.5 * 10-4 cm2 V-1 s-1 at elec. fields >=105 V/cm. The transport is relatively field independent and weakly temp. dependent, pointing to a high degree of chem. regioregularity and purity. These factors make poly(3-hexylthiophene) attractive for use in a range of electronic applications.