Abstract
The application of silicon oxide (SiOx)-based anode materials in lithium-ion batteries is hampered by their low conductivity and large volume expansion. To tackle both issues, ultrafine SiOx/C composite nanospheres with a uniform diameter of similar to 40 nm were fabricated through a tri-component co-assembly approach. The ultrafine SiOx/C nanospheres demonstrated a high specific capacity of 895 mA h g(-1) after 200 cycles at 200 mA g(-1). At a high current density of 1 A g(-1), a capacity of 828 mA h g(-1 )could be achieved after 1000 cycles. The ultrafine SiOx/C nanospheres were further assembled into pomegranate-like assemblies through spray drying. The resultant pomegranate-like structure manifested a discharge capacity of 1024 mA h g(-1 )after 200 cycles at 500 mA g(-1).