Abstract
The oral drug delivery system using bilayer (or multilayer) tablets has been more commonly used in therapeutic strategies. However, one of the most common problems associated with bilayer tablets is the insufficient interfacial strength between layers, which leads to product failure during manufacturing. Therefore, it is important to better understand the interfacial strength of bilayer pharmaceutical tablets. For this purpose, in this study, the interfacial strength of bilayer tablets made of microcrystalline cellulose (MCC PH 102) at various manufacturing conditions was systematically examined. Three cases were considered to explore: (1) the effect of interfacial curvature on the interfacial strength, for which the interfaces between two layers with different curvatures were produced using flat, convex and concave punches. (2) The effect of water content on the interfacial strength, for which the powder was conditioned at various relative humidity before being used to produce bilayer tablets. (3) The effect of the particle size of the powder used in first layer on the interfacial strength, for which the feed powder was sieved to obtain powders with specific particle sizes that were then used to produce the first layer of the bilayer tablets. For all cases considered, direct tensile tests were performed to measure the tablet interfacial strength. It is found that the interfacial curvature, the water content and the particle size in the first layer affected the interfacial strength significantly. It is also shown that the tablet interfacial strength was increased when larger particles were used in the first layer, or when curved punches (i.e. either convex or concave punches) were used to produce curved interfaces with increased interfacial areas. In addition, a higher interfacial strength can also be achieved by properly controlling water content in the powder.
[Display omitted]
•Interfacial strength of bilayer tablets were directly measured using the direct tensile test.•The impact of moisture content, particle size and interface curvature on the interfacial strength was explored.•The interfacial strength was increased when larger particles were used for the first layer.•The interfacial strength was increased when curved punches were used to produce curved interfaces with increased interfacial area.•A higher interfacial strength can also be achieved with properly controlling the water content.